Anatase

TiO2 Content: min 98.5%; CIE L*: min 98.5; Reducing power: min 110; Oil absorption: max 22 g/100g; Sieve(325 mesh) %: max. 0.05; Moisture @ 105℃ %: max. 0.4.

Bluish undertone with high gloss; High whiteness; Good hiding power and lightening power; Excellent dispersibility

Multifunctional applications such as Paint, Color Master, Chemical fiber, Rubber .

Rutile

TiO2 Content: min 97%; CIE L*: min 98; Reducing power (TCS): min 1900; Oil absorption: max 16 g/100g

Alumina surface treatment； Bluish undertone； High gloss； Low reactivity with antioxidants

Masterbatch; Styrene plastic (PS); Rigid and flexible PVC; ABS compound; PE

Rutile

TiO2 Content: min 97%; CIE L*: min 98; Reducing power (TCS): min 2000; Oil absorption: max 14 g/100g

Alumina surface treatment； Bluish undertone； High gloss

Masterbatch； Engineering plastic； Film； Fiber

Rutile

TiO2 Content: min 94%; CIE L*: min 98; Reducing power (TCS): min 2000; Oil absorption: max 20 g/100g

Alumina-silicon surface treatment; Warm undertone; Good hiding power and high whiteness

Window profiles & sidings; Tubes; Silage & greenhouse films; Garden furniture & WPC composites; Synthetic turf; Tarpaulins & roofings; Membranes

Rutile

TiO2 Content: min 94%; CIE L*: min 98; Reducing power (TCS): min 2000; Oil absorption: max 20 g/100g

Economic； Bluish undertone； Excellent tint reducing power and opacity； High durability, heat and light resistance； High gloss and hiding power； Good dispersibility

Industrial coatings； Solvent paints； Printing ink

Rutile

TiO2 Content: min 94%; CIE L*: min 98; Reducing power (TCS): min1950; Oil absorption: max 18 g/100g

Alumina-zirconia surface treatment； Bluish undertone； Good hiding power

Because with high gloss, for high-end coatings, paints industry, and high-end ink industry.

Rutile

TiO2 Content: min 94%; CIE L*: min 98.5; Reducing power (TCS): min 2000; Oil absorption: max 18 g/100g

Alumina-zirconia surface treatment； Bluish undertone； High gloss； Good hiding power

Because with high gloss, for high-end coatings, paints industry, and high-end ink industry.

Rutile

TiO2 Content: min 90%; Oil absorption: max 24 g/100g; Light fastness DIN54004: min 6

Alumina-phosphorus surface treatment； High gloss； Good hiding power； Bluish undertone

mainly used in high and low pressure decorative paper, pre-impregnated foils, melamine and urea formaldehyde resin impregnation etc.

Rutile

TiO2 Content: min 94%; CIE L*: min 98; Reducing power (TCS): min 2000; Oil absorption: max 20 g/100g

Alumina-silicon surface treatment; Bluish undertone; Good hiding power and high whiteness

Window profiles & sidings; Tubes; Membranes; Garden furniture & WPC composites; Silage & greenhouse films; Synthetic turf; Tarpaulins & roofings

Rutile

TiO2– content (%): min. 92 ； Inorganic treatment : Al2O3, SiO2 ； Organic Processing: Polyol ； Color coordinate L* : min. 98 ； Rel. lightening Power (TCS): min. 2000 ； Background color (SCX): min. 3.7

Bluish undertone； High gloss； Good hiding power； Excellent dispersibility

Industrial coatings; Water base coating; Ink; Rubber